Composite Supporting Bracket
INTRODUCTIONCharacteristics
Light Weight
UV Corrosion Resistance
High Strength
Acid and Alkali Corrosion
Application
Technical Parameters
| Properties | Typical Value |
| Fiber Volume Contant(%) | 75% |
| Identity(G/cm3) | 2.1 |
| Properties | Value | Test Standard |
| 0° Tensile Modulus(Gpa) | 40 | GB/T 1447-2005 |
| 0° Tensile Strength(Mpa) | 800 | GB/T 1447-2005 |
| 0° Compression Strength(Mpa) | 800 | GB/T 1448-2005 |
| 0° Compression Modulus(Gpa) | 40 | GB/T 1448-2005 |
| 0° Flexural Modulus(Mpa) | 35 | GB/T 9341-2008 |
| 0° Flexural Strength(Mpa) | 800 | GB/T 9341-2008 |
| Shear Strength(Mpa) | 60 | GB/T 1450 |
| 0° Bolt Extrusion Strength(Mpa) | 100 | ASTM D5961 |
| 90° Bolt Extrusion Strength(Mpa) | 180 | ASTM D5961 |
| Screw Drawing Capacity(KN) | 5 | ASTM D7332 |
Note: Typical value is affected by the test method.